Synthesis and Characterization of ZnO Nanoparticles and Their Application on Cotton Fabrics to Obtain Superhydrophobic Surfaces

Main Article Content

Mai Ebrahim
https://orcid.org/0009-0000-2377-2466
Ziad Saffour

Abstract

Zinc oxide nanoparticles were synthesized in a wet chemical manner at two different reaction temperatures 30, 90 ̊C utilizing zinc chloride as precursors in an aqueous medium. Zinc oxide nanoparticles were characterized by scanning electron microscopy (SEM), X-ray analysis (XRD), and infrared spectroscopy (FTIR). X-ray patterns pointed to a Wurtzite structure with an average crystalline size of 19.5 nm and 23 nm for the ZnO NPs synthesis at 30 ̊C and 90 ̊C, respectively. SEM showed that with increasing temperature, the morphology of Zinc oxide nanoparticles changed from nanowire to spherical structures.


To fabricate super hydrophobic cotton fabric, the fabric was immersed in a colloidal solution of ZnO NPs with a concentration of 1% and then modified later with stearic acid. The samples were characterized by scanning electron microscopy (SEM) and contact angle (CA) test. The SEM results showed that the ZnO NPs synthesis at 90 ̊C created a rough structure on the cotton surface better than that of ZnO synthesis at 30 ̊C. The CA test showed super hydrophobic properties for ZnO@90˚C samples, while ZnO@30˚C samples showed hydrophobic properties only after modified stearic acid.


Different stearic acid concentrations were used for the hydrophobization of the ZnO surface. (CA) results revealed that the fabric treated with ZnO NPs prepared at  90°C and modified with 1% by weight of stearic acid showed a superhydrophobic surface at a contact angle (CA = 154°).

Article Details

How to Cite
1.
Synthesis and Characterization of ZnO Nanoparticles and Their Application on Cotton Fabrics to Obtain Superhydrophobic Surfaces. Baghdad Sci.J [Internet]. 2024 Aug. 1 [cited 2024 Dec. 6];21(8):2635. Available from: https://bsj.uobaghdad.edu.iq/index.php/BSJ/article/view/8934
Section
article

How to Cite

1.
Synthesis and Characterization of ZnO Nanoparticles and Their Application on Cotton Fabrics to Obtain Superhydrophobic Surfaces. Baghdad Sci.J [Internet]. 2024 Aug. 1 [cited 2024 Dec. 6];21(8):2635. Available from: https://bsj.uobaghdad.edu.iq/index.php/BSJ/article/view/8934

References

Jaafar HT, Aldabbagh BMD. Investigation of superhydrophobic/hydrophobic materials properties using electrospinning technique. Baghdad Sci J. 2019; 16(3): 632-638. https://doi.org/10.21123/bsj.2019.16.3.0632.‏

He Y, Wan M, Wang Z, Zhang X, Zhao Y, Sun L. Fabrication and characterization of degradable and durable fluoride-free super-hydrophobic cotton fabrics for oil/water separation. Surf Coat Technol. 2019; 378: 125079. https://doi.org/10.1016/j.surfcoat.2019.125079. ‏

Sushanta S, Smita M, Sanjay KN. Superhydrophobic Polymer Coatings. Elsevier; 2019. Chap 3, Methods and fabrication techniques of superhydrophobic surfaces p 43-68.https://doi.org/10.1016/B978-0-12-816671-0.00004-7.

Williams JT. Waterproof and water repellent textiles and clothing. Woodhead Publ. 2018. Chap 11, Superhydrophobicity; p 267-297. https://doi.org/10.1016/B978-0-08-101212-3.00010-1.

Tudu BK, Sinhamahapatra A, Kumar A. Surface modification of cotton fabric using TiO2 nanoparticles for self-cleaning, oil–water separation, anti-stain, anti-water absorption, and antibacterial properties. ACS omega. 2020; 5(14): 7850-7860. https://doi.org/10.1021/acsomega.9b04067. ‏

Guo Y, Li C, Li X, Xu H, Chen W, Fang K, et al. Fabrication of superhydrophobic cotton fabric with multiple durability and wearing comfort via an environmentally friendly spraying method. Ind Crops Prod.2023; 194: 116359. ‏ https://doi.org/10.1016/j.indcrop.2023.116359.

Pour FZ, Karimi H, Avargani VM. Preparation of a superhydrophobic and superoleophilic polyester textile by chemical vapor deposition of dichlorodimethylsilane for Water–Oil separation. Polyhedron. 2019; 159: 54-63. ‏ https://doi.org/10.1016/j.poly.2018.11.040 .

Espanhol-Soares M, Costa L, Silva MRA, Soares Silva F, Ribeiro LMS, Gimenes R. Super-hydrophobic coatings on cotton fabrics using sol–gel technique by spray. J Solgel Sci Technol.2020; 95: 22-33. https://doi.org/10.1007/s10971-020-05307-x.

Lai Y, Guo Y, Xu L, Chang X, Zhang X, Xu G, et al. Plasma enhanced fluorine-free superhydrophobic polyester (PET) fabric with ultra-robust antibacterial and antibacterial adhesion properties. Coatings. 2020; 11(1): 15. https://doi.org/10.3390/coatings11010015.

Raha S, Ahmaruzzaman M. ZnO nanostructured materials and their potential applications: progress, challenges, and perspectives. Nanoscale. 2022; 4(8): 1868-1925. https://doi.org/10.1039/D1NA00880C.

Sharma P, Hasan MR, Mehta NK, Bishoyi A, Narang J. 92 years of zinc oxide: has been studied by the scientific community since the 1930s-an overview. Sensors. 2022; 3: 100182. https://doi.org/10.1016/j.sintl.2022.100182.

Alwash A. The green synthesize of zinc oxide catalyst using pomegranate peels extract for the photocatalytic degradation of methylene blue dye. Baghdad Sci J. 2020; 17(3): 787- 794. http://dx.doi.org/10.21123/bsj.2020.17.3.0787.

Verbič A, Gorjanc M, Simončič B. Zinc oxide for functional textile coatings: Recent advances. Coatings. 2019; 9(9): 550. ‏ https://doi.org/10.3390/coatings9090550.

Kumar V, Gowri S, Prabhakar P, Sen R K, Uppal N, Khan M A, et al. Development of superhydrophobic cotton fabric using zinc oxide nanoflower/polydimethylsiloxane (PDMS) nanocomposite coatings. Text Leather Rev. 2021; 4(4): 253-266. ‏‏ https://doi.org/10.31881/TLR.2021.18.

Patil GD, Patil AH, Jadhav SA, Patil CR, Patil PS. A new method to prepare superhydrophobic cotton fabrics by post-coating surface modification of ZnO nanoparticles. Mater Lett. 2019; 255: 126562. ‏ https://doi.org/10.1016/j.matlet.2019.126562.

Wang M, Peng M, Weng YX, Li YD, Zeng JB. Toward durable and robust superhydrophobic cotton fabric through hydrothermal growth of ZnO for oil/water separation. Cellulose.2019; 26: 8121-8133. ‏https://doi.org/10.1007/s10570-019-02635-2.

Perillo PM, Atia MN, Rodríguez DF. Effect of the reaction conditions on the formation of the ZnO nanostructures. Physica E Low Dimens Systnano struct. 2017; 85: 185-192. https://doi.org/10.1016/j.physe.2016.08.029.

Chen H, Muros-Cobos JL, Amirfazli. A Contact angle measurement with a smartphone. Rev Sci Instrum. 2018; 89(3): 035117. https://doi.org/10.1063/1.5022370.

Kayani ZN, Saleemi F, Batool I. Effect of calcination temperature on the properties of ZnO nanoparticles. Appl Phys. 2015; 119: 713-720. ‏https://doi.org/10.1007/s00339-015-9019-1.

Koutu V, Shastri L, Malik MM. Effect of temperature gradient on zinc oxide nanoparticles synthesized at low reaction temperatures. Mater Res Express. 2017; 4(3): 035011.https://doi.org/10.1088/2053-1591/aa5855 ‏.

Wasly HS, El-Sadek MA, Henini M. Influence of reaction time and synthesis temperature on the physical properties of ZnO nanoparticles synthesized by the hydrothermal method. Appl Phys. 2018; 124:1-12. https://doi.org/10.1007/s00339-017-1482-4

Saffar MA, Eshaghi A, Dehnavi MR. Superhydrophobic ZnO thin film modified by stearic acid on copper substrate for corrosion and fouling protections. J Solgel Sci Technol. 2022; 100(3): 672-682. https://doi.org/10.1007/s10971-022-05749-5

Zhu W, Wu Y, Zhang Y. Synthesis and characterisation of superhydrophobic CNC/ZnO nanocomposites by using stearic acid. Micro Nano Lett.2019; 14(13): 1317-1321. https://doi.org/10.1049/mnl.2019.0335.

Similar Articles

You may also start an advanced similarity search for this article.